Electrode has excellent welding properties, good slag removal and minimum spatter.The weld metal is very resistant to hot crack.
Product Name Corrosion Resisting Low Alloy Steel Electrode
Product No. MHAE411-WE025
Standard
GB AWS JIS DIN
E5518-W
E8018-W2
Type of Covering Iron powder Low hydrogen Potassium
Welding Position F,V, OH,H
Chemical Composition of Deposited Metal (%)
Chemical Composition C Mn Si S P Cr Ni Mo V Cu
Guarantee ≤0.12
0.055
0.50-1.30
1.00 0.35-0.80
0.55 ≤0.03
0.013 ≤0.03
0.018 0.45-0.70
0.60
0.40-0.80
0.65 — — 0.30-0.75
0.48
Mechanical Properties of Deposited Metal
Test Item Tensile Strengh
Rm (MPa) Yield point
ReL (MPa)
Elongation
A4 (%) Akv1(J)
Guarantee ≥550
610 ≥460
500 ≥19
23 -20°C ≥27 82
Reference Current (AC or DC)
Electrode Diameter(mm) 2.5 3.2 4.0 5.0
Welding Current(A) 70-110 100-140 140-170 190-240
Instructions
1.The Electrodes must be baked under 300~350 for an hour before Welding and used as soon as baking is completed.
2.The stains on the weldments, such as rust, oil stains, moisture, etc., must be cleared away before Welding.
3.When Welding, short arc must be used and stringer bead is suitable.
Application
Suitable for welding structrues made by atmospheric corrosion and infection resistance steels, e.g. ASTM A424 & A588 steels.
Product Name Corrosion Resisting Low Alloy Steel Electrode
Product No. MHAE411-WE025
Standard
GB AWS JIS DIN
E5518-W
E8018-W2
Type of Covering Iron powder Low hydrogen Potassium
Welding Position F,V, OH,H
Chemical Composition of Deposited Metal (%)
Chemical Composition C Mn Si S P Cr Ni Mo V Cu
Guarantee ≤0.12
0.055
0.50-1.30
1.00 0.35-0.80
0.55 ≤0.03
0.013 ≤0.03
0.018 0.45-0.70
0.60
0.40-0.80
0.65 — — 0.30-0.75
0.48
Mechanical Properties of Deposited Metal
Test Item Tensile Strengh
Rm (MPa) Yield point
ReL (MPa)
Elongation
A4 (%) Akv1(J)
Guarantee ≥550
610 ≥460
500 ≥19
23 -20°C ≥27 82
Reference Current (AC or DC)
Electrode Diameter(mm) 2.5 3.2 4.0 5.0
Welding Current(A) 70-110 100-140 140-170 190-240
Instructions
1.The Electrodes must be baked under 300~350 for an hour before Welding and used as soon as baking is completed.
2.The stains on the weldments, such as rust, oil stains, moisture, etc., must be cleared away before Welding.
3.When Welding, short arc must be used and stringer bead is suitable.
Application
Suitable for welding structrues made by atmospheric corrosion and infection resistance steels, e.g. ASTM A424 & A588 steels.
Certificate