Ceramic-Rubber-Liner
300*150*63 mm Hot Vulcanizing Resistant Rubber Ceramic Wear Liner
Product ID: 2 Rubber Wear Liner
Send Inquiry
Ceramic material
92% alumina
Ceramic size
147*97*50mm*3 pieces
Rubber wear liner size
300*150*63mm
Rubber wear liner size weight
About 9.0kg/piece
Sample time
1-5 days
Al2O3:≥92% Density:≥3.6g/cm³
Porosity:<0.25 compressive strength:≥1050Mpa Rockwell Harndess ≥85.5HRA Vickers Hardness Hv20:
≥1050Mpa Fracture Toughness(KIC): ≥3.7MPa.m1/2 Bending strength: ≥220Mpa Wear Volume:≤0.25cm3 Appearance: white
Rubber:Natural Tensile strength(TSB):≥15Mpa Shore A Hardness: 50-60 Thermal conductivity.(normal temperature): 2w/m·k Adhesive
between tile and rubber: 3.8Mpa Elongation: 468% Resilience:0.65
Steel Thickness: 6mm Steel: Q235A or Q235B Q235A: C 0.14-0.22% Mn 0.30-0.65% Si≤0.30 S≤0.050 P≤0.045 Q235B: C 0.12-0.20% Mn
0.30-0.670% Si≤0.30 S≤0.045 P≤0.045
92% alumina
Ceramic size
147*97*50mm*3 pieces
Rubber wear liner size
300*150*63mm
Rubber wear liner size weight
About 9.0kg/piece
Sample time
1-5 days
Al2O3:≥92% Density:≥3.6g/cm³
Porosity:<0.25 compressive strength:≥1050Mpa Rockwell Harndess ≥85.5HRA Vickers Hardness Hv20:
≥1050Mpa Fracture Toughness(KIC): ≥3.7MPa.m1/2 Bending strength: ≥220Mpa Wear Volume:≤0.25cm3 Appearance: white
Rubber:Natural Tensile strength(TSB):≥15Mpa Shore A Hardness: 50-60 Thermal conductivity.(normal temperature): 2w/m·k Adhesive
between tile and rubber: 3.8Mpa Elongation: 468% Resilience:0.65
Steel Thickness: 6mm Steel: Q235A or Q235B Q235A: C 0.14-0.22% Mn 0.30-0.65% Si≤0.30 S≤0.050 P≤0.045 Q235B: C 0.12-0.20% Mn
0.30-0.670% Si≤0.30 S≤0.045 P≤0.045
Certificate
- Three system certification
Main Products
ceramic rubber plate,flat ceramic tiles, mosaic tiles